| UBE Nylon 1013B (Dry) UBE Nylon 1013B is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated Chemical Resistant Good Mold Release Heat Resistant Impact Resistant&&UBE Nylon 1013B Low viscosity (Injection)&& |
| Product Description | |
|---|---|
| Supplier | UBE |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Low Viscosity,noise reduction,Good stripping performance,Self-lubricating,High Heat Resistance,Good wear resistance,Grease resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| yield | 80 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| fracture | 40 | % | ISO 527-1/2 |
| Tensile modulus | 2900 | MPa | ISO 527-1-2 |
| bending strength | 110 | MPa | ISO 178 |
| Bending modulus | 2700 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| M-level | 80 | ISO 2039-2 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 215~225 | ℃ | ISO 11357 |
| Linear coefficient of thermal expansion | 8 | x10-5/℃ | ISO 11359-2 |
| Hot deformation temperature | |||
| 0.45 MPa | 155 | ℃ | ISO 75-1/2 |
| 1.8 MPa | 60 | ℃ | ISO 75-1/2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 10^15 | ohms·cm | JIS K6911 |
| Dielectric strength | 20 | kV/mm | IEC 60243-1 |
| Relative permittivity | 3.5 | IEC 60250 | |
| Arc resistance | 119 | sec | ASTM D495 |
| Compared to the leakage tracing index | 0 | UL index | UL746A |
| other | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | 2.5 | % | UBE 方法 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5 | ISO 179-1eA |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shrinkage rate | |||
| MD | 1.4 | % | Internal Method |
| TD | 1.5 | % | Internal Method |
| Density | 1.14 | g/cm³ | ISO 1183-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 220 | °C | |
| Barrel middle temperature | 230 | °C | |
| Barrel front temperature | 245 | °C | |
| Nozzle temperature | 245 | °C | |
| Processing (melt) temperature | 250 | °C | |
| Mold temperature | 70 to 80 | °C | |
| Injection pressure | 63.7 | MPa | |
| Back pressure | 9.80 | MPa | |
| Screw speed | 100 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |