| SUMIKASUPER® LCP E5002L is a Liquid Crystal Polymer (LCP) material filled with glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of SUMIKASUPER® LCP E5002L: Flame Rated.&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low Viscosity,High Heat Resistance,Good wear resistance,Solvent resistance,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ASTM D792 |
| Shrinkage rate | Internal Method | ||
| MD | 0.070 | % | Internal Method |
| TD | 1.3 | % | Internal Method |
| Water absorption rate | |||
| saturated | 0.020 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 150 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.7 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 9510 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 23 ℃ | 127 | MPa | ASTM D790 |
| Poisson’s ratio | 0.51 | ASTM E132 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 180 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 6.4 mm | 480 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 354 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | Internal Method | ||
| MD：150℃ | 2.0E-6 | 1/℃ | Internal Method |
| TD：150℃ | 8.1E-5 | 1/℃ | Internal Method |
| Thermal conductivity coefficient | 0.44 | W/m/K | JIS R2618 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric constant | ASTM D150 | ||
| 1 MHz | 3.40 | ASTM D150 | |
| 1.00 GHz | 3.10 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 1 MHz | 0.023 | ASTM D150 | |
| 1 GHz | 4.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.30 mm, all colors | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Soldering Resistance | 350 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 | °C | |
| Drying time | 4.0 to 24 | hr | |
| Barrel rear temperature | 350 to 370 | °C | |
| Barrel middle temperature | 370 to 390 | °C | |
| Barrel front temperature | 390 to 410 | °C | |
| Nozzle temperature | 390 to 410 | °C | |
| Processing (melt) temperature | 400 | °C | |
| Mold temperature | 40 to 160 | °C | |
| Injection pressure | 120 to 160 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |