| DIOFAN® 193 D is a PVDC latex recommended for use as a functional topcoat over DIOFAN® A736 coated PVC or PVC/PE film structures used for blister applications in pharmaceutical packaging.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDC |
| Material Status | Commercial: Active |
| Features | Low odor,Moisture resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| PH value | Acidic | ||
| surface tension | |||
| Foaming trend | 32 | mN/m | |
| Film-forming property | |||
| Minimum film-forming temperature | 18 | ℃ | |
| Solid content | 55 | % | |
| Density | |||
| Disperse (wet) | 1.290 | g/cm³ | |
| coating | 1.650 | g/cm³ | |
| Lotion type | 阴离子 | ||
| viscosity | |||
| 20℃ | 0.011 | Pa·s | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| &Metal – Dynamic | 0.20 | mN/m | Internal Method |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen transfer rate | |||
| 25℃，85% RH，1.0 µm | 54 | cm³/m²/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 38℃，90% RH，1.0 µm | 16 | g/m²/24 hr | ASTM F1249 |
| Maximum heat sealing resistance | |||
| with Aluminum 20 psi 1s 1 heated jaw，140℃ | 5.8 | N/cm |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Shelf life – Latex | |||
| 23℃ | 12 | month |
| Notes |
|---|
| 1. with limitation |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. Tested on PVC (250 µm)/Diofan® A736 (32 gsm)/Diofan® 193 D (8 gsm) structure stored at 40°C for 2 days. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |