| ZENITE® SEA20N is a 40% mineral filled grade. It offers excellent surface appearance, low warpage, and excellent dimensional stability. Application for this grade is compact camera module, and other thin, small electronic parts&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Low warping,Good surface appearance,Good Dimensional Stability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.77 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.76 | % | ISO 294-4 |
| MD | 0.25 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 105 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 4.2 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 10000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 126 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 220 | ℃ | ISO 75-2/A |
| Melting temperature | 330 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 6.0 | hr | |
| Barrel rear temperature | 310 to 320 | °C | |
| Barrel middle temperature | 320 to 330 | °C | |
| Barrel front temperature | 330 to 350 | °C | |
| Nozzle temperature | 330 to 340 | °C | |
| Processing (melt) temperature | 335 to 345 | °C | |
| Mold temperature | 80 to 140 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Injection speed | Moderate-Fast | ||
| Hold pressure | 50.0 to 150 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |