| About |
|---|
| NYCOA 2301 is a highly flexible Nylon copolymer TPE suitable for extrusion processing and injection molding. NYCOA 2301 processes easily at low injection pressure compared to other impact modified nylons. It can be molded and extruded on standard equipment. NYCOA 2301 is recommended for applications that require premium toughness such as hoses, connectors, tool housing, appliance parts, and hardware items.&& |
| Product Description | |
|---|---|
| Generic | PA+TPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 1.2 | % | ASTM D955 |
| TD | 1.4 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 1.7 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 52.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 300 | % | ASTM D638 |
| Bending modulus | 896 | MPa | ASTM D790 |
| bending strength | 35.9 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 212 | ℃ | DSC |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 216 to 227 | °C | |
| Barrel middle temperature | 221 to 238 | °C | |
| Barrel front temperature | 232 to 249 | °C | |
| Nozzle temperature | 243 to 260 | °C | |
| Processing (melt) temperature | 243 to 254 | °C | |
| Mold temperature | 21 to 49 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |