| About |
|---|
| Stylac™ IB331 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, or Europe. Characteristics include: Heat Resistant High Viscosity&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Ultra High Viscosity,Heat Resistance, Good |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 1.8 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 1.90 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 17 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 95.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 116 | ℃ | ISO 306/B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 2.50 mm | 107 | ||
| tensile strength | |||
| yield | 50.0 | MPa | ISO 527-2/50 |
| Bending modulus | 2650 | MPa | ISO 178 |
| bending strength | 86.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |