| About |
|---|
| DENKA Transparent Polymer TX-100S is a Methyl Methacrylate Styrene (MMS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Denka |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Europe,Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 200℃，49N | 1.8 | g/10min | ISO 1133 |
| Density | 1127 | kg/m³ | ISO 1183 |
| Molding shrinkage | 0.4 | % | Internal Method |
| Water Absorption | |||
| 24 H, balanced Equilibrium | 0.12 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld, 50 mm/min | 67 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| 2 mm/min | 3400 | MPa | ISO 178 |
| Flexural Strength | |||
| 2 mm/min | 115 | MPa | ISO 178 |
| Rockwell hardness | 84 | M Scale | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa | 79 | ℃ | ISO 75-1/-2 |
| Vicat Softening Temperature | 100 | ℃ | ISO 306/B |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Light Transmission | 92 | % | ISO 13468-1 |
| Haze | 0.2 | % | ISO 14782 |
| Refractive Index | 1.54 | % | ASTM D542 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 70-80 | ℃ | |
| Drying Time | 3-4 | hr | |
| Cylinder Temperature | 190-240 | ℃ | |
| Nozzle temperature | 220-240 | ℃ | |
| Mold Temperature | 40-70 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. NA*D ray |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |