| Panlite® L-1225L is a Polycarbonate (PC) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Panlite® L-1225L are: Flame Rated Good Mold Release Low Viscosity Typical application of Panlite® L-1225L: Automotive&& |
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity,Good stripping performance,High infrared light transmittance,HB,V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD：4.0 mm | 0.50 to 0.70 | % | Internal Method |
| MD：4.0 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 61.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2/50 |
| Bending modulus | 2350 | MPa | ISO 178 |
| bending strength | 93.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 67 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | No Break | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 126 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 139 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 146 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| RTI Elec（1.5 mm） | 125 | ℃ | UL 746 |
| RTI Imp（1.5 mm） | 115 | ℃ | UL 746 |
| RTI Str（1.5 mm） | 125 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 30 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.10 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 9.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.90 mm | HB | UL 94 | |
| 0.40 mm | V-2 | UL 94 | |
| Burning wire flammability index | IEC 60695-2-12 | ||
| 1.5 mm | 850 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Hot filament ignition temperature | IEC 60695-2-13 | ||
| 1.5 mm | 875 | ℃ | IEC 60695-2-13 |
| 3.0 mm | 850 | ℃ | IEC 60695-2-13 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.585 | ASTM D542 | |
| Transmittance | |||
| 3000 µm | 88.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. short time test |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |