| AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance Technical components of cooling water cycles in the automotive industry.&& |
| Product Description | |
|---|---|
| Generic | PA610 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Solvent resistance,Low moisture absorption |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | |
| Spiral flow length | 40.0 | cm | |
| Water absorption rate | |||
| 70℃，62% RH | 1.2 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 12 | kJ/m² | |
| 23℃ | 16 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 110 | kJ/m² | |
| 23℃ | 110 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 200 | ℃ | |
| 8.0 MPa, unannealed | 140 | ℃ | |
| Melting temperature | 220 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | ||
| Burning rate | |||
| 1 mm | < 100 | mm/min |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ash Content | 30 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H 961/30 | 195 | MPa | |
| Tensile modulus | 8600 | MPa | |
| tensile strength | |||
| fracture | 160 | MPa | |
| Tensile strain | |||
| fracture | 5.5 | % | |
| Bending modulus | 7700 | MPa | |
| bending strength | 230 | MPa | |
| Fracture bending strain | 5.5 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mold Temperature: 176°F, Melt Temperature: 518°F, Injection Pressure: 1.09E+4 psi |
| 3. cross section of flow spiral: 7 mm x 3.5 mm |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 7. >1 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |