| About |
|---|
| Orgalloy® RS 66 series is a rigid polyamide 66 alloy. Outstanding properties: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties. The grade referenced: non-reinforced grade for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA66 Alloy |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Electroplating |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 0.70 | % | ISO 62 |
| 23℃，50% RH | 1.2 | % | ISO 62 |
| Water absorption rate | 2.9 | % | ISO 62 |
| Melt Flow Rate | |||
| 235℃，5.0kg | 15 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 80.0 | ℃ | ISO 75-2/Af |
| Melting temperature | 255 | ℃ | ISO 11357-3 |
| Vicat Softening Temp | |||
| B50 | 165 | ℃ | ISO 306/A50 |
| A50 | 225 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ISO 11359-2 |
| TD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 6.0E+15 | Ω.cm | IEC 60093 |
| Surface resistance | 2.5E+16 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 1.00 mm | 36.0 | KV/mm | IEC 60243-1 |
| Dissipation factor | |||
| 0.025 | IEC 60250 | ||
| 0.017 | IEC 60250 | ||
| 0.032 | 1 kHz | IEC 60250 | |
| Compared to the leakage tracing index | >=600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| – | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 17 | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179/Af |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 77 | ISO 868 | |
| tensile strength | |||
| Yield, 23 ℃, 50 mm/min | 51.5 | MPa | ISO 527-2 |
| 23℃ | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃, 50 mm/min | >=100 | % | ISO 527-2 |
| Yield, 23 ℃, 50 mm/min | 4.1 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃，1 mm/min | – | MPa | ISO 527-2 |
| Tensile creep modulus | |||
| 1 Hr | 2270 | MPa | ISO 899-1 |
| 1000 Hr | – | MPa | ISO 899-1 |
| bending strength | |||
| 23 ℃, 50% RH, after adjustment | 67.0 | MPa | ISO 178 |
| 23℃ | 75.0 | MPa | ISO 178 |
| Bending modulus | |||
| Adjusted 50% RH and 23 ℃ | 2100 | MPa | ISO 178 |
| 23℃ | 2300 | MPa | ISO 178 |
| Elastic modulus | 2600 | MPa | ISO R527 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |