| PBT+PET含有15%玻纤增强材料，模具释放，热稳定，可用于食品接触 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Heat Stabilized,Glass fiber reinforced |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| 5 mm/min | |||
| 5 mm/min | |||
| Tensile strain | |||
| yield | 90 | MPa | ASTM D 638 |
| 5 mm/min | |||
| fracture | 90 | MPa | ASTM D 638 |
| 5 mm/min | |||
| Tensile modulus | |||
| 5 mm/min | 5000 | MPa | ASTM D638 |
| Bending modulus | |||
| 4500 | MPa | ASTM D790 | |
| yield | 3 | % | ASTM D 638 |
| Tensile modulus | |||
| fracture | 3 | % | ASTM D 638 |
| 1 mm/min | 5400 | MPa | ISO 527 |
| bending strength | |||
| Yield, 2 mm/min | 145 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 4700 | MPa | ISO 178 |
| yield | 95 | MPa | ISO 527 |
| fracture | 95 | MPa | ISO 527 |
| yield | 3 | % | ISO 527 |
| fracture | 3 | % | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 35 | J/m | ASTM D256 |
| -30℃ | 30 | J/m | ASTM D256 |
| 23℃，80*10*4 | 6 | kJ/m² | ISO 180-1A |
| 80*10*4 -30℃ | 5 | kJ/m² | ISO 180-1A |
| Instrument control anti impact total energy 23 ℃ | 6 | J | ASTM D 3763 |
| Charpy Notched Impact Strength | |||
| 23 ℃, 80 * 10 * 3, 62mm span | 5 | kJ/m² | ISO 179/1eA |
| Notched impact strength of cantilever beam | |||
| 23℃，80*10*4 | 30 | kJ/m² | ISO 180/1U |
| -30℃，80*10*4 | 25 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 185 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 100 mm span | 175 | ℃ | ISO 75/Ae |
| 1.8 MPa, unannealed, 3.2 mm | 160 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 4.5E-05 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 5.4E-05 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 5.5E-05 | 1/℃ | ISO 11359-2 |
| TD：23~80℃ | 8.5E-05 | 1/℃ | ISO 11359-2 |
| Vicat Softening Temp | |||
| B50 | 185 | ℃ | ISO 306 |
| B120 | 190 | ℃ | ISO 306 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.4-1 | % | Internal Method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.26 | % | ISO 62 |
| 23℃，50% RH | 0.06 | % | ISO 62 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 12 | cm³/10min | ISO 1133 |
| Melt Flow Rate | |||
| 265℃，1.20kg | 16 | g/10min | ASTM D1238 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2-6 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 260-285 | °C | |
| Nozzle temperature | 265-275 | °C | |
| Front temperature | 260-280 | °C | |
| Mid section temperature | 250-270 | °C | |
| Post stage temperature | 240-260 | °C | |
| Hopper temperature | 40-60 | °C | |
| Mold temperature | 60-110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |