| PAXOTHENE NA112-27 (LDPE) possesses low melt index and good toughness especially suitable for films with thickness of 0.020~0.100 mm. The said films are for package of shopping bags, frozen bags, re-closable bags and shrink packaging applications. NA112-27 is formulated with medium slip to give good openability of film. High gloss and low haze characteristics of blown film made from NA112-27 provide attractive appearance to the packaged goods thus more valuable.&& |
| Product Description | |
|---|---|
| Supplier | USI |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good surface appearance,Food contact compliance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | 3.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 52 | ASTM D2240 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D882 | ||
| MD, yield | 8.92 | MPa | ASTM D882 |
| TD, yield | 8.92 | MPa | ASTM D882 |
| MD, fracture | 18.6 | MPa | ASTM D882 |
| TD, fracture | 15.1 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 340 | % | ASTM D882 |
| TD, fracture | 550 | % | ASTM D882 |
| Drop hammer impact | 110 | g | ASTM D1709 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 |
| Melting peak temperature | 108 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 100 | ASTM D523 | |
| Haze | 7.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |