| About |
|---|
| Westlake EMAC® Plus SP1501 is a 20% EMA copolymer designed for extrusion coating, compounding and blending where low viscosity, flexibility and strength are important. SP1501 provides excellent elasticity and low temperature performance. This resin is capable of very high filler loadings. A higher peak melting temperature than comparable EMA grades makes it a more viable choice for building products that are subjected to 180°F testing.&& |
| Product Description | |
|---|---|
| Supplier | Westlake Chemical |
| Generic | EMA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Low Viscosity,Good bond |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.941 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 25 | g/10min | ASTM D1238 |
| Methacrylic acid content | 20.0 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 37 | ASTM D2240 | |
| tensile strength | |||
| fracture | 5.52 | MPa | ASTM D638 |
| yield | 3.86 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 480 | % | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -73.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 43.0 | ℃ | ASTM D1525 |
| Melting peak temperature | 100 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |