| FS-10-VO-200-P is a short glass fiber reinforced, flame retardant, diallyl meta-phthalate molding compound, which meets the requirements of ASTM D5948 Type SIG-F.&& |
| Product Description | |
|---|---|
| Supplier | SBHPP |
| Generic | DAP增塑剂 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.91 | g/cm³ | ASTM D792 |
| Apparent density | 0.80 | g/cm³ | ASTM D1895 |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | ASTM D955 |
| Water absorption rate | |||
| 48hr | 0.25 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 76.0 | MPa | ASTM D638 |
| Bending modulus | 11700 | MPa | ASTM D790 |
| bending strength | 131 | MPa | ASTM D790 |
| compressive strength | 152 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 32 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 260 | ℃ | ASTM D648-A |
| Linear coefficient of thermal expansion | |||
| MD | 1.8E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | 130 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 15 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 3.90 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.016 | ASTM D150 | |
| Arc resistance | 175 | sec | ASTM D495 |
| Compared to the leakage tracing index | > 600 | V | IEC 60112，ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Extreme oxygen index | 50 | % | ASTM D2863 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B (Step-by-Step) |
| 3. Wet, 60 Hz |
| 4. Wet |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |