| Unreinforced, neat PBT resin for fibers. Natural Color Only, Not intended for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2500 | MPa | ASTM D638 |
| Tensile modulus | 2600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 50.0 | MPa | ASTM D638 |
| fracture | 45.0 | MPa | ISO 527-2/50 |
| yield | 50.0 | MPa | ASTM D638 |
| yield | 45.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 1.8 | % | ISO 527-2/50 |
| fracture | 2.0 | % | ASTM D638 |
| yield | 1.8 | % | ISO 527-2/50 |
| yield | 2.0 | % | ASTM D638 |
| Bending modulus | 2290 | MPa | ISO 178 |
| 50 mm span | 2390 | MPa | ASTM D790 |
| bending strength | 81.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 84.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 28 | J/m | ASTM D256 |
| 23℃ | 2.9 | kJ/m² | ISO 180-1A |
| 23℃ | 890 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 35 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 5.00 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 51.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 48.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 113 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 104 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 178 | ℃ | ISO 306 |
| B120 | 177 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 8.5E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 8.5E-5 | 1/℃ | ISO 11359-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ASTM D792 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，1.20kg | 130 | g/10min | ASTM D1238 |
| Melt Volume Rate | ISO 1133 | ||
| 250℃，1.2 kg | 127 | cm³/10min | ISO 1133 |
| 250℃，2.16 kg | 231 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 1.6 to 2.0 | % | Internal Method |
| MD：3.2 mm | 1.5 to 1.8 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.080 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.070 | % | ISO 62 |
| Apparent viscosity of melt | 35.0 | Pa·s | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 200 to 230 | °C | |
| Barrel 2 zone temperature | 240 to 255 | °C | |
| Barrel 3 zone temperature | 240 to 275 | °C | |
| Barrel 4 zone temperature | 240 to 275 | °C | |
| Connector temperature | 240 to 275 | °C | |
| Melt temperature | 245 to 260 | °C | |
| Nozzle temperature | 240 to 275 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |