| About |
|---|
| SABIC® LDPE PCG09 SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG09 is an additive free grade, typically designed for healthcare packaging and can typically be converted by Injection Molding and Cast Film to produce caps and closures, small bottles and secondary packaging. Compliance to Regulations SABIC® LDPE PCG09 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).&&SABIC® LDPE PCG09 Low density polyethylene for Healthcare Description SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG09 is an additive free grade, typically designed for healthcare packaging and can typically be converted by Injection Molding and Cast Film to produce caps and closures, small bottles and secondary packaging. Compliance to Regulations SABIC® LDPE PCG09 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | High purity,Low density |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 7.5 | g/10min | |
| 190℃，5.0kg | 25 | g/10min | |
| Melt Volume Rate | ISO 1133 | ||
| 190℃，2.16 kg | 10.0 | cm³/10min | |
| 190℃，5 kg | 33.0 | cm³/10min | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30 ℃, injection molding | 8.0 | kJ/m² | |
| 23 ℃, injection molding | 50 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 46.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 93.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 110 | ℃ | DIN 53765 |
| Enthalpy Change | 138 | J/g | DIN 53765 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | 41 | ISO 868 | |
| Tensile modulus | |||
| injection molding | 170 | MPa | ISO 527-2/1A/50 |
| tensile strength | ISO 527-2/1A/50 | ||
| Yield, injection molding | 9.00 | MPa | |
| Fracture, injection molding | 10.0 | MPa | |
| Tensile strain | |||
| Fracture, injection molding | 100 | % | ISO 527-2/1A/50 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Conditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |