| About |
|---|
| High Flow, High Stiffness Interior TPO Suitable for Seamless Airbag Applications&& |
| Product Description | |
|---|---|
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High liquidity,Ductility |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 19.0 | MPa | ISO 527-2 |
| Bending modulus | 1900 | MPa | ISO 178 |
| Anti scratch | > 15 | N | FLTM BN108-13 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 8.0 | kJ/m² | |
| 23℃ | 48 | kJ/m² | |
| Dart impact equipped with measuring instruments | |||
| -30℃，Energy to Peak Load | 23.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 107 | ℃ | ISO 75-2/B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 179 | °C | |
| Barrel middle temperature | 191 to 199 | °C | |
| Barrel front temperature | 210 | °C | |
| Nozzle temperature | 199 | °C | |
| Processing (melt) temperature | 188 to 216 | °C | |
| Mold temperature | 48.9 to 60.0 | °C | |
| Injection speed | 慢to中等 | ||
| Cushion | 10.0 to 20.0 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 22.0 ft/sec |
| 3. # Ductile 30/30 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |