| About |
|---|
| LNP LUBRILOY* D2000 is a compound based on Polycarbonate resin containing a Proprietary Non-Halogenated Lubrication System. Added feature of this material is: Wear Resistant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | HB,Good stripping performance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 1.17 | g/cm³ | ASTM D792 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.80 | % | ASTM D955 |
| MD：24 hrs | 0.80 | % | ASTM D955 |
| TD：24 hrs | 0.81 | % | ISO 294-4 |
| MD：24 hrs | 0.84 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.18 | % | ISO 62 |
| 24hr，50% RH | 0.14 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2050 | MPa | ASTM D638 |
| Tensile modulus | 2090 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 58.0 | MPa | ISO 527-2/5 |
| fracture | 46.0 | MPa | ASTM D638 |
| yield | 59.0 | MPa | ISO 527-2/5 |
| yield | 57.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 170 | % | ISO 527-2/5 |
| fracture | 47 | % | ASTM D638 |
| yield | 6.1 | % | ASTM D638 |
| yield | 6.6 | % | ISO 527-2/5 |
| Bending modulus | 1970 | MPa | ISO 178 |
| 50 mm span | 2170 | MPa | ASTM D790 |
| bending strength | 77.0 | MPa | ISO 178 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.31 | ASTM D3702 Modified | |
| static state | 0.22 | ASTM D3702 Modified | |
| Wear factor | |||
| Washer | 38.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | No Break | ASTM D4812 | |
| 23℃ | 690 | J/m | ASTM D256 |
| 23℃ | 60 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 50.0 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 42.0 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 128 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 131 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 139 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 142 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-30~30℃ | 7.6E-5 | 1/℃ | ASTM D696 |
| MD：-30~30℃ | 7.5E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Temperature at the rear of the barrel | 293 to 304 | °C | |
| Temperature in the middle of the barrel | 299 to 310 | °C | |
| Front temperature of material barrel | 304 to 316 | °C | |
| Processing (melt) temperature | 304 to 316 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Modified: Manual |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |