| About |
|---|
| 未增强的PC + PET合金。优良的低温、耐化学性和良好的高温性能。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Good surface appearance,Good liquidity,Good color stability,High Heat Resistance,Solvent resistance,low-temperature impact resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Yield, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 110 | % | ASTM D638 |
| bending strength | |||
| Yield, 1.30 mm/min, 50 mm span | 86 | MPa | ASTM D790 |
| Bending modulus | |||
| 1.3 mm/min，50mm跨距 | 2130 | MPa | ASTM D790 |
| Instrument impact energy peak | |||
| 23℃ | 54 | J | ASTM D 3763 |
| -30℃ | 61 | J | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 129 | ℃ | ASTM D648 |
| 1.8 MPa | 112 | ℃ | ASTM D648 |
| Linear expansion coefficient, -40 ℃ to 95 ℃ | |||
| flow | 9.E-05 | 1/℃ | ASTM E 831 |
| TD | 9.18E-05 | 1/℃ | ASTM E 831 |
| Relative temperature index | |||
| Electrical performance | 75 | ℃ | UL 746B |
| Impact mechanical performance | 75 | ℃ | UL 746B |
| Non mechanical impact performance | 75 | ℃ | UL 746B |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ASTM D792 |
| Specific volume | 0.83 | cm³/g | ASTM D 792 |
| Water absorption rate | |||
| 24hr | 0.16 | % | ASTM D570 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5-0.8 | % | Internal Method |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | |||
| Tungsten wire | 6 | PLC Code | ASTM D495 |
| Hot wire ignition {PLC} | 2 | PLC Code | UL 746A |
| High voltage arc marking rate {PLC} | 3 | PLC Code | UL 746A |
| High current arc ignition (surface {PLC}) | 0 | PLC Code | UL 746A |
| Compared to the leakage tracing index | 3 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.47 mm | HB | UL 94 | |
| CSA | LS88480 | 文件号 | CSA |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 747 | J/m | ASTM D256 |
| -30℃ | 464 | J/m | ASTM D256 |
| -40℃ | 299 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4 – 6 | hrs | |
| Drying time (cumulative) | 8 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 260 – 280 | °C | |
| Nozzle temperature | 255 – 275 | °C | |
| Front temperature | 260 – 280 | °C | |
| Mid section temperature | 255 – 275 | °C | |
| Post stage temperature | 250 – 270 | °C | |
| Mold temperature | 65 – 95 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 50 – 80 | rpm | |
| Shoot to cylinder size | 50 – 80 | % | |
| Depth of exhaust groove | 0.013 – 0.02 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |