| About |
|---|
| Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold release.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Steam sterilized,Biocompatible,Moderate liquidity,Ethylene oxide disinfection |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 7.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | |
| MD：3.2 mm | 0.50 to 0.70 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2350 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 63.0 | MPa | |
| fracture | 70.0 | MPa | |
| Tensile strain | |||
| yield | 6.0 | % | |
| fracture | 120 | % | |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 10.0 | mg | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 15 | kJ/m² | ISO 179/1eA |
| 23℃ | 75 | kJ/m² | ISO 179/1eA |
| 23℃ | 35 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 15 | kJ/m² | |
| 23℃ | 75 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 138 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 127 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| B50 | 144 | ℃ | ISO 306 |
| B120 | 145 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 123~127℃ | 通过 | ||
| 140℃ | 通过 | ||
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 7.0E-5 | 1/℃ | |
| TD：23~80℃ | 7.0E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| Relative temperature index | 125 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 125 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 50 Hz | 2.70 | ||
| 60 Hz | 2.70 | ||
| 1 MHz | 2.70 | ||
| Dissipation factor | |||
| 50 Hz | 1.0E-3 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 0.010 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glowing wire flammability index | |||
| 1.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ISO 489 | |
| Transmittance | |||
| 2540 µm | 89.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | < 0.80 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 270 to 300 | °C | |
| Barrel middle temperature | 280 to 310 | °C | |
| Barrel front temperature | 290 to 320 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 290 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. at Yield |
| 5. 80*10*3 sp=62mm |
| 6. 80*10*3 mm |
| 7. 120*10*4 mm |
| 8. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |