| Orgalloy® RS 6635A是一种聚酰胺66合金（尼龙66合金）产品,含有的填充物为填料。 它可以通过型材挤出成型、挤出、树脂传递成型或注射成型进行加工,在亚太地区、北美洲、拉丁美洲、欧洲或非洲和中东有供货。 主要特性为:耐热。&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA66 Alloy |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Electroplating,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ISO 1183-2 |
| Melt Volume Rate | |||
| 275℃，2.16 kg | 6.00 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| saturated | 1.7 | % | ISO 62-2 |
| balance | 0.70 | % | ISO 62-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | — | MPa | ISO 527-2 2 |
| tensile strength | |||
| fracture | — | MPa | ISO 527-2 2 |
| Tensile strain | |||
| fracture | — | % | ISO 527-2 2 |
| Tensile Creep Modulus（1 hr） | — | MPa | ISO 899-1 2 |
| Tensile creep modulus | |||
| 1000 hr | — | MPa | ISO 899-1 2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 225 | ℃ | ISO 75-2 2 |
| 0.45 MPa | 245 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | |||
| B50 | 200 | ℃ | ISO 306 2 |
| Melting temperature | 255 | ℃ | ISO 11357-3 2 |
| Linear coefficient of thermal expansion | |||
| TD | 1.0E-4 | 1/℃ | ISO 11359-2 2 |
| MD | 1.7E-5 | 1/℃ | ISO 11359-2 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | IEC 60093 2 |
| Volume resistivity | — | ohms·m | IEC 60093 2 |
| Dielectric strength | 34 | kV/mm | IEC 60243-1 2 |
| Relative permittivity | |||
| 100 Hz | — | IEC 60250 2 | |
| 1 MHz | — | IEC 60250 2 | |
| Dissipation factor | |||
| 100 Hz | — | IEC 60250 2 | |
| 1 MHz | — | IEC 60250 2 | |
| Compared to the leakage tracing index | |||
| CTI | — | IEC 60112 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | ISO 1210 2 | |
| Flame retardant level | |||
| 3.20 mm | HB | ISO 1210 2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |