| About |
|---|
| AKROLOY® PA GF 60 black (2844) is a 60% glass fibre reinforced polyamide blend with very high stiffness and strength, even in conditioned state. This material is listet at UL at 0,8 mm all colors HB. Components with high dimensional stability, independent from moisture content. AKROLOY PA GF 60 is an alternative for aluminium- and zinc diecast alloys.&& |
| Product Description | |
|---|---|
| Generic | PA 66+PA 6I/6T |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.72 | g/cm³ | ISO 1183 |
| Spiral flow length | 47.0 | cm | Internal Method |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.50 | % | ISO 294-4 |
| MD | < 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 3.0 to 3.5 | % | ISO 62 |
| 70℃，62% RH | 0.80 | % | ISO 1110 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 14 | kJ/m² | ISO 179/1eA |
| 23℃ | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 90 | kJ/m² | ISO 179/1eU |
| 23℃ | 100 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 225 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 245 | ℃ | ISO 75-2/B |
| Melting temperature | 255 | ℃ | DIN EN 11357-1 |
| Linear coefficient of thermal expansion | |||
| TD：23~80℃ | 5.5E-5 | 1/℃ | ISO 11359-2 |
| MD：23~80℃ | 1.5E-5 | 1/℃ | ISO 11359-2 |
| Temperature index | IEC 216 | ||
| 50% tensile strength loss, 20000 hr | 110 to 130 | ℃ | IEC 216 |
| 50% tensile strength loss, 5000 hr | 140 to 150 | ℃ | IEC 216 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 | |
| Burning rate | |||
| 1 mm | < 100 | mm/min | FMVSS 302 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ash Content | 60 | % | ISO 1172 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 21000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 275 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2/5 |
| Bending modulus | 20000 | MPa | ISO 178 |
| bending strength | 405 | MPa | ISO 178 |
| Ball hardness | |||
| H 961/30 | 330 | MPa | ISO 2039-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mold Temperature: 212°F, Melt Temperature: 608°F, Injection Pressure: 1.09E+4 psi |
| 3. cross section of flow spiral: 7 mm x 3.5 mm |
| 4. 0.079 in/min |
| 5. 10°C/min |
| 6. >1 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |