| About |
|---|
| High performance polymer, Polyetheretherketon (PEEK) for thermally and chemically stressed parts&& |
| Product Description | |
|---|---|
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Solvent resistance,Heat Stabilized,V-0 |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 95.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 50 ℃ | 4.7 | % | ISO 527-2/23 |
| bending strength | |||
| 23℃，4 mm | 115 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 4.0 mm | 155 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 340 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| 1 mm | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | |||
| 1.0 mm | > 1.0E+15 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.75 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 355 to 375 | °C | |
| Mold temperature | 100 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80x10x4 mm |
| 3. 110x10x4 mm |
| 4. Compound for molding, 10k/min |
| 5. 80x80x1 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |