| About |
|---|
| PA6, 30% 玻纤增强 , 低温冲击改性 , 适用于注塑 , 黑色 |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | low-temperature impact resistance,Glass fiber reinforced |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 1 mm/min | 8700 | MPa | ISO 527 |
| Tensile fracture strength | |||
| 5 mm/min | 150 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 5 mm/min | 3.6 | % | ISO 527 |
| Tensile yield strength | |||
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 221 | ℃ | ISO 11357-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 100 | kJ/m² | ISO 179/1eU |
| -30℃ | 90 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| -30℃ | 12 | kJ/m² | ISO 179/1eA |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：23℃，72 hrs，50% RH | 0.40 – 0.60 | % | ISO 2577 |
| TD：23℃，72 hrs，50% RH | 0.90 – 1.10 | % | ISO 2577 |
| Melt Volume Rate | |||
| 275℃，5 kg | 25 | cm³/10min | ISO 1133 |
| Process Conditions | |||
|---|---|---|---|
| Processing conditions | Nominal value | Unit | Test method |
| Pre drying temperature/time | 75-85°C / 2-4h | ||
| Recommended melting temperature | 250-290 | °C | |
| Recommended mold temperature | 80-100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |