Marvel™ M3504DXP

About
M3504DXP and Marvel M50 are powder and compounded form of Dowlex NG2429 which are linear-low density polyethylene octene copolymer for rotational molding applications. M3504DXP is a natural color available in powder form, which are specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and long life expectancy. Both of them are recommended for large and thick tanks with a generous radius and curve.&&

About

M3504DXP and Marvel M50 are powder and compounded form of Dowlex NG2429 which are linear-low density polyethylene octene copolymer for rotational molding applications. M3504DXP is a natural color available in powder form, which are specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and long life expectancy. Both of them are recommended for large and thick tanks with a generous radius and curve.&&

Product Description
Supplier	SCG
Generic	PE
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Low warping,Excellent Processability,Good flexibility,Renewable resources,Food contact compliance,Good color stability,Octene copolymer,Heat Stabilized,High ESCR
Availabilitys	North America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.935	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	4.0	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
100% emulsifier, F50	> 1000	hr	ASTM D1693

IMPACT	Nominal value	Unit	Test method
ARM impact (-20 ℃)	230	J/cm	ISO 6603-2

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	75.0	℃	ASTM D648
Vicat Softening Temp	118	℃	ISO 306/A120
Melting temperature	125	℃	DSC
Crystallization peak temperature
DSC	105	℃	ISO 3146

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	57		ISO 868
tensile strength			ISO 527-2
yield	17.0	MPa	ISO 527-2
fracture	25.0	MPa	ISO 527-2
Tensile strain
fracture	800	%	ISO 527-2
Bending modulus
1% secant	640	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.