| About |
|---|
| Features Exceptionally tough and durable Resists breakage and handles challenging functional assemblies Great for snap fits, assemblies and demanding applications Ideal for master patterns for vacuum casting&& |
| Product Description | |
|---|---|
| Generic | 3D打印材料 |
| Material Status | Commercial: Active |
| Features | Ultra high toughness,Durability |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.12 | g/cm³ | |
| — | 1.18 | g/cm³ | |
| Water absorption rate | |||
| balance | 0.38 | % | ASTM D570 |
| viscosity | |||
| 30℃ | 0.65 to 0.75 | Pa·s | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 55 to 66 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 47.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 42.0 | ℃ | ASTM D648 |
| Glass transition temperature | 52.0 | ℃ | DMA |
| Linear coefficient of thermal expansion | |||
| MD | ASTM E831 | ||
| 30 to 50 ℃ | 9.5E-5 | cm/cm/℃ | ASTM E831 |
| 70 to 140 ℃ | 1.8E-4 | cm/cm/℃ | ASTM E831 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Critical Exposure | 8.30 | mJ/cm² | |
| Penetration depth | 116.8 | µm |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 78 to 80 | ||
| Tensile modulus | 2300 to 2630 | MPa | ASTM D638 |
| tensile strength | 45.0 to 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 7.0 to 20 | % | ASTM D638 |
| Bending modulus | 2350 to 2550 | MPa | ASTM D790 |
| bending strength | 75.0 to 79.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Liquid, 25°C |
| 3. Solid, 25°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |