Vectra® B230 - SOLIAO

About
Exceptional strength and stiffness. Suitable for metal replacement applications. Electrically conductive. 30% carbon fiber reinforced. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 at 0.46mm thickness per UL 94 flame testing. Relative- Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C. UL = Underwriters Laboratories (USA)&&

About

Exceptional strength and stiffness. Suitable for metal replacement applications. Electrically conductive. 30% carbon fiber reinforced. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 at 0.46mm thickness per UL 94 flame testing. Relative- Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C. UL = Underwriters Laboratories (USA)&&

Product Description
Supplier	Celanese
Generic	液态聚合物
Material Status	Commercial: Active
Features	Good Rigidity,Conductive,Halogen free,Flame Characteristics,V-0
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.49	g/cm³	ISO 1183
Shrinkage rate			Internal Method
TD：1.00 mm	0.18	%
MD：1.0 mm	-0.050	%
Water absorption rate
23℃，24hr	0.080	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
tensile strength	245	MPa	ASTM D638
Tensile strain
fracture	0.90	%	ASTM D638
Bending modulus	30000	MPa	ISO 178
bending strength	300	MPa	ISO 178
Bending strain	1.1	%	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	6.0	kJ/m²	ISO 179-1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	240	℃	ISO 75-2/A

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	7.0E+2	ohms·cm	Internal Method

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	V-0		UL 94

Supplementary information	Nominal value	Unit	Test method
Color Number	BK430P

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.