Adflex Q 108 F

About
Adflex Q 108 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. It is suitable for the extrusion and calendering of soft film and sheet, for the impact modification of polypropylene and other compounding applications, as well as monolayer and multilayer air quenched blown films. It is also used by our customers for automotive color-matched interior trim applications. The grade is available in natural pellet form and has no slip or antiblock, and only minimal stabilization in order to allow wider design latitude for the compounder. Additional suitable stabilization is recommended to protect the resin during melt processing and throughout its useful life.&&

About

Adflex Q 108 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. It is suitable for the extrusion and calendering of soft film and sheet, for the impact modification of polypropylene and other compounding applications, as well as monolayer and multilayer air quenched blown films. It is also used by our customers for automotive color-matched interior trim applications. The grade is available in natural pellet form and has no slip or antiblock, and only minimal stabilization in order to allow wider design latitude for the compounder. Additional suitable stabilization is recommended to protect the resin during melt processing and throughout its useful life.&&

Product Description
Supplier	LyondellBasell
Generic	Polyolefin Elastomer
Material Status	Commercial: Active
Features	Good flexibility,High impact resistance,Low Hardness,Heat Resistance, Good,Puncture Resistant,High ESCR,Good coloring,Low Gloss
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.880	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	0.60	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	30		ISO 868
tensile strength
fracture	11.0	MPa	ISO 527-2
Tensile strain
fracture	> 500	%	ISO 527-2
Bending modulus	80.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/1A
-40 ℃, localized fracture	6.0	kJ/m²	ISO 180-1A
-20℃	No Break		ISO 180/1A
23℃	No Break		ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	40.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	60.0	℃	ISO 306/A50
Melting temperature	142	℃	ISO 11357-3

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.