| AVP™ GLT25CP是一种聚碳酸脂 + PET (PC+PET)产品,。 它可以通过注射成型进行加工,在北美洲有供货。 主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 35 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.60 to 0.90 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.18 mm | 56.5 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 110 | % | ASTM D638 |
| Bending modulus | |||
| 3.18 mm | 2410 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 86.2 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 530 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.35 mm | 116 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.5 mm，ALL EXC NC | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended injection volume | 50 to 80 | % | |
| Barrel rear temperature | 254 to 268 | °C | |
| Barrel middle temperature | 254 to 268 | °C | |
| Barrel front temperature | 260 to 274 | °C | |
| Nozzle temperature | 254 to 268 | °C | |
| Processing (melt) temperature | 266 to 279 | °C | |
| Mold temperature | 66 to 88 | °C | |
| Back pressure | 0.172 to 0.345 | MPa | |
| Screw speed | 25 to 50 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |