| About |
|---|
| Stat-Rite® S-102 is a static dissipative Polyethylene alloy. Stat-Rite® S-102 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. It is specially developed for blown film applications and is highly suitable for ESD-sensitive parts requiring a robust packaging that does not tear easily. FEATURES Clean, permanent, and more consistent than anti-stat Provides protection for many years Robust APPLICATIONS Semiconductor packaging Electronic component packaging Hard disk drive packaging&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | PE alloy |
| Material Status | Commercial: Active |
| Features | High purity,Rapid Static Decay,Electrostatic discharge protection,Good tear strength,Antistatic property |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 15.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 8.0E+9 | ohms·cm | ESD S11.12 |
| Electrostatic attenuation | |||
| 1000V to 10V | < 2.0 | sec | CPM |
| Surface resistance | 4.0E+8 | ohms | ESD S11.11 |
| Tribocharge（Nitrile Gloves） | < 20.0 | V | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 60.0 µm | 84.0 | % | ASTM D1003 |
| Haze | |||
| 60 µm | 37 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ion content | Internal Method | ||
| Br Anion：60.0 µm | < 0.0100 | µg/cm² | Internal Method |
| Cl Anion：60.0 µm | < 0.0100 | µg/cm² | Internal Method |
| F Anion：60.0 µm | < 0.0100 | µg/cm² | Internal Method |
| NO2 Anion：60.0 µm | < 0.0100 | µg/cm² | Internal Method |
| NO3 Anion：60.0 µm | < 0.0100 | µg/cm² | Internal Method |
| PO4 Anion：60.0 µm | < 0.0100 | µg/cm² | Internal Method |
| SO4 Anion：60.0 µm | < 0.0100 | µg/cm² | Internal Method |
| Outgassing | Internal Method | ||
| Hydrocarbons：60.0 µm | 445 | ng/cm² | Internal Method |
| Phenols：60.0 µm | 22.0 | ng/cm² | Internal Method |
| Total Outgassing：60.0 µm | 467 | ng/cm² | Internal Method |
| Filler | IDP Alloy |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test Method #3010-4 |
| 3. Test Method #3010-3 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |