| LNP THERMOCOMP LF003 is a compound based on Polyetheretherketone resin containing 15% Glass Fiber.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ASTM D792 |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 1.0 | % | ASTM D955 |
| MD：24 hrs | 0.80 | % | ASTM D955 |
| TD：24 hrs | 1.0 | % | ISO 294-4 |
| MD：24 hrs | 0.79 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6930 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 137 | MPa | ASTM D638 |
| fracture | 125 | MPa | ISO 527-2 |
| yield | 137 | MPa | ASTM D638 |
| yield | 125 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.4 | % | ISO 527-2 |
| fracture | 3.1 | % | ASTM D638 |
| yield | 2.9 | % | ASTM D638 |
| yield | 2.4 | % | ISO 527-2 |
| Bending modulus | 7000 | MPa | ISO 178 |
| bending strength | 200 | MPa | ASTM D790 |
| bending strength | 209 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 850 | J/m | ASTM D4812 |
| 23℃ | 53 | J/m | ASTM D256 |
| 23℃ | 6.6 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 54 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 14.6 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 3.10 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 244 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 259 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 325 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 329 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 3.1E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 3.1E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 4.8E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 4.9E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 370 to 380 | °C | |
| Barrel middle temperature | 380 to 400 | °C | |
| Barrel front temperature | 380 to 400 | °C | |
| Mold temperature | 175 to 190 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 60 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type 1A |
| 4. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |