Texin 285 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 85A. It can be processed by injection molding, extrusion, and blow molding.&&

Product Description
Supplier	Covestro
Generic	TPU-酯
Material Status	Commercial: Active
Features	Good flexibility,High impact resistance,Good wear resistance,HB,V-2
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.20	g/cm³	ASTM D792
Density	1.20	g/cm³	ISO 1183
Shrinkage rate			ISO 2577
TD：2.54 mm	0.80	%	ASTM D955
MD：2.54 mm	0.80	%	ASTM D955
TD：2.54 mm	0.80	%	ISO 2577
MD：2.54 mm	0.80	%	ISO 2577

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	85		ASTM D2240
Shaw’s A	85		ISO 868
Bending modulus			ASTM D790
-30℃	49.6	MPa	ASTM D790
23℃	27.6	MPa	ASTM D790
Bending modulus			ISO 178
-30℃	49.6	MPa	ISO 178
23℃	27.6	MPa	ISO 178
Taber abraser
1000 cycles, 1000 g, H-18 wheels	35.0	mg	ISO 4649
1000 cycles, 1000 g, H-18 wheels	35.0	mg	ASTM D1044

elastic body	Nominal value	Unit	Test method
tensile strength
yield	37.9	MPa	ISO 37
yield	37.9	MPa	ASTM D412
300% strain	13.1	MPa	ISO 37
300% strain	13.1	MPa	ASTM D412
100% strain	5.30	MPa	ISO 37
100% strain	5.30	MPa	ASTM D412
50% strain	5.00	MPa	ISO 37
50% strain	5.00	MPa	ASTM D412
Tensile strain
fracture	500	%	ISO 37
fracture	500	%	ASTM D412
tear strength	87.6	kN/m	ASTM D624
tear strength	88	kN/m	ISO 34-1
Compression deformation			ASTM D395B
23℃，22 hr	12	%	ASTM D395B
23℃，22 hr	16	%	ASTM D395B
70℃，22 hr	35	%	ASTM D395B
70℃，22 hr	65	%	ASTM D395B
Compression deformation			ISO 815
23℃，22 hr	16	%	ISO 815
23℃，22 hr	12	%	ISO 815
70℃，22 hr	65	%	ISO 815
70℃，22 hr	35	%	ISO 815
Basho’s elasticity	45	%	ASTM D2632

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -68.0	℃	ASTM D746
Embrittlement temperature	< -68.0	℃	ISO 974
Glass transition temperature	-42.0	℃	DMA
Vicat Softening Temp	91.0	℃	ASTM D1525 4
Vicat Softening Temp	91.0	℃	ISO 306/50
Relative temperature index
Electrical performance, 1.50 mm	50.0	℃	UL 746
Strength mechanical performance, 1.50 mm	50.0	℃	UL 746
Impact mechanical performance, 1.50 mm	50.0	℃	UL 746

Aging performance	Nominal value	Unit	Test method
The rate of change in tensile strength in air			ASTM D573
100℃，70 hr	20	%	ASTM D573
100% Strain，100℃，70 hr	-2.0	%	ASTM D573
300% Strain，100℃，70 hr	14	%	ASTM D573
100℃，168 hr	10	%	ASTM D573
100% Strain，100℃，168 hr	-1.0	%	ASTM D573
300% Strain，100℃，168 hr	12	%	ASTM D573
100℃，336 hr	14	%	ASTM D573
100% Strain，100℃，336 hr	-2.0	%	ASTM D573
300% Strain，100℃，336 hr	9.0	%	ASTM D573
100℃，504 hr	6.0	%	ASTM D573
100% Strain，100℃，504 hr	-3.0	%	ASTM D573
300% Strain，100℃，504 hr	12	%	ASTM D573
The rate of change in tensile strength in air			ISO 216
100℃，70 hr	20	%	ISO 216
100% Strain 100℃，70 hr	-2.0	%	ISO 216
300% Strain 100℃，70 hr	14	%	ISO 216
100℃，168 hr	10	%	ISO 216
100% Strain 100℃，168 hr	-1.0	%	ISO 216
300% Strain 100℃，168 hr	12	%	ISO 216
100℃，336 hr	14	%	ISO 216
100% Strain 100℃，336 hr	-2.0	%	ISO 216
300% Strain 100℃，336 hr	9.0	%	ISO 216
100℃，504 hr	6.0	%	ISO 216
100% Strain 100℃，504 hr	-3.0	%	ISO 216
300% Strain 100℃，504 hr	12	%	ISO 216
The rate of change in ultimate elongation in air			ASTM D573
100℃，70 hr	5.0	%	ASTM D573
100℃，168 hr	8.0	%	ASTM D573
100℃，336 hr	16	%	ASTM D573
100℃，504 hr	14	%	ASTM D573
Changes in tensile stress during fracture in air			ISO 216
100℃，70 hr	5.0	%	ISO 216
100℃，168 hr	8.0	%	ISO 216
100℃，336 hr	16	%	ISO 216
100℃，504 hr	14	%	ISO 216
The rate of change in hardness of a hardness tester in the air			ASTM D573
Shore D, 100 ℃, 70 hr	-3.0		ASTM D573
Shore D, 100 ℃, 168 hr	-3.0		ASTM D573
Shore D, 100 ℃, 336 hr	-3.0		ASTM D573
Shore D, 100 ℃, 504 hr	-3.0		ASTM D573
The rate of change of Shore hardness in air			ISO 216
Shore D, 100 ℃, 70 hr	-3.0		ISO 216
Shore D, 100 ℃, 168 hr	-3.0		ISO 216
Shore D, 100 ℃, 336 hr	-3.0		ISO 216
Shore D, 100 ℃, 504 hr	-3.0		ISO 216
The rate of change in tensile strength			ASTM D471
23℃，70 hr，in Reference Fuel A（Isooctane）	11	%	ASTM D471
100% Strain，23℃，70 hr，in Reference Fuel A（Isooctane）	-3.0	%	ASTM D471
300% Strain，23℃，70 hr，in Reference Fuel A（Isooctane）	-4.0	%	ASTM D471
23 ℃, 70 hr, methanol	-18	%	ASTM D471
100% Strain，23℃，70 hr，in Reference Fuel C	-7.0	%	ASTM D471
300% Strain，23℃，70 hr，in Reference Fuel C	-20	%	ASTM D471
23℃，168 hr，in Reference Fuel A（Isooctane）	10	%	ASTM D471
100% Strain，23℃，168 hr，in Reference Fuel A（Isooctane）	-2.0	%	ASTM D471
300% Strain，23℃，168 hr，in Reference Fuel A（Isooctane）	-2.0	%	ASTM D471
23 ℃, 168 hr, methanol	-20	%	ASTM D471
100% Strain，23℃，168 hr，in Reference Fuel C	-6.0	%	ASTM D471
300% Strain，23℃，168 hr，in Reference Fuel C	-20	%	ASTM D471
23℃，336 hr，in Reference Fuel A（Isooctane）	16	%	ASTM D471
100% Strain，23℃，336 hr，in Reference Fuel A（Isooctane）	7.0	%	ASTM D471
300% Strain，23℃，336 hr，in Reference Fuel A（Isooctane）	3.0	%	ASTM D471
23℃，336 hr，in Reference Fuel C	-18	%	ASTM D471
100% Strain，23℃，336 hr，in Reference Fuel C	-7.0	%	ASTM D471
300% Strain，23℃，336 hr，in Reference Fuel C	-19	%	ASTM D471
23℃，504 hr，in Reference Fuel A（Isooctane）	20	%	ASTM D471
100% Strain，23℃，504 hr，in Reference Fuel A（Isooctane）	1.0	%	ASTM D471
300% Strain，23℃，504 hr，in Reference Fuel A（Isooctane）	-1.0	%	ASTM D471
23℃，504 hr，in Reference Fuel C	-18	%	ASTM D471
100% Strain，23℃，504 hr，in Reference Fuel C	-6.0	%	ASTM D471
300% Strain，23℃，504 hr，in Reference Fuel C	-18	%	ASTM D471
100 ℃, 70 hr, in ASTM # 1 oil	20	%	ASTM D471
100% Strain，100℃，70 hr，in ASTM #1 Oil	-5.0	%	ASTM D471
300% Strain，100℃，70 hr，in ASTM #1 Oil	10	%	ASTM D471
100 ℃, 70 hr, in ASTM # 3 oil	30	%	ASTM D471
100% Strain，100℃，70 hr，in ASTM #3 Oil	-8.0	%	ASTM D471
300% Strain，100℃，70 hr，in ASTM #3 Oil	12	%	ASTM D471
100℃，168 hr，in ASTM #1 Oil	9.0	%	ASTM D471
100% Strain，100℃，168 hr，in ASTM #1 Oil	-1.0	%	ASTM D471
300% Strain，100℃，168 hr，in ASTM #1 Oil	10	%	ASTM D471
100℃，168 hr，in ASTM #3 Oil	30	%	ASTM D471
100% Strain，100℃，168 hr，in ASTM #3 Oil	-6.0	%	ASTM D471
300% Strain，100℃，168 hr，in ASTM #3 Oil	13	%	ASTM D471
100℃，336 hr，in ASTM #1 Oil	7.0	%	ASTM D471
100% Strain，100℃，336 hr，in ASTM #1 Oil	-2.0	%	ASTM D471
300% Strain，100℃，336 hr，in ASTM #1 Oil	10	%	ASTM D471
100℃，336 hr，in ASTM #3 Oil	30	%	ASTM D471
100% Strain，100℃，336 hr，in ASTM #3 Oil	-9.0	%	ASTM D471
300% Strain，100℃，336 hr，in ASTM #3 Oil	7.0	%	ASTM D471
100℃，504 hr，in ASTM #1 Oil	1.0	%	ASTM D471
100% Strain，100℃，504 hr，in ASTM #1 Oil	-4.0	%	ASTM D471
300% Strain，100℃，504 hr，in ASTM #1 Oil	10	%	ASTM D471
100℃，504 hr，in ASTM #3 Oil	7.0	%	ASTM D471
100% Strain，100℃，504 hr，in ASTM #3 Oil	-6.0	%	ASTM D471
300% Strain，100℃，504 hr，in ASTM #3 Oil	9.0	%	ASTM D471
The rate of change in tensile strength			ISO 175
23℃，70 hr，in Reference Fuel A（Isooctane）	11	%	ISO 175
100% Strain，23℃，70 hr，in Reference Fuel A（Isooctane）	-3.0	%	ISO 175
300% Strain，23℃，70 hr，in Reference Fuel A（Isooctane）	-4.0	%	ISO 175
23 ℃, 70 hr, methanol	-18	%	ISO 175
100% Strain，23℃，70 hr，in Reference Fuel C	-7.0	%	ISO 175
300% Strain，23℃，70 hr，in Reference Fuel C	-20	%	ISO 175
23℃，168 hr，in Reference Fuel A（Isooctane）	10	%	ISO 175
100% Strain，23℃，168 hr，in Reference Fuel A（Isooctane）	-2.0	%	ISO 175
300% Strain，23℃，168 hr，in Reference Fuel A（Isooctane）	-2.0	%	ISO 175
23 ℃, 168 hr, methanol	-20	%	ISO 175
100% Strain，23℃，168 hr，in Reference Fuel C	-6.0	%	ISO 175
300% Strain，23℃，168 hr，in Reference Fuel C	-20	%	ISO 175
23℃，336 hr，in Reference Fuel A（Isooctane）	16	%	ISO 175
100% Strain，23℃，336 hr，in Reference Fuel A（Isooctane）	7.0	%	ISO 175
300% Strain，23℃，336 hr，in Reference Fuel A（Isooctane）	3.0	%	ISO 175
23℃，336 hr，in Reference Fuel C	-18	%	ISO 175
100% Strain，23℃，336 hr，in Reference Fuel C	-7.0	%	ISO 175
300% Strain，23℃，336 hr，in Reference Fuel C	-19	%	ISO 175
23℃，504 hr，in Reference Fuel A（Isooctane）	20	%	ISO 175
100% Strain，23℃，504 hr，in Reference Fuel A（Isooctane）	1.0	%	ISO 175
300% Strain，23℃，504 hr，in Reference Fuel A（Isooctane）	-1.0	%	ISO 175
23℃，504 hr，in Reference Fuel C	-18	%	ISO 175
100% Strain，23℃，504 hr，in Reference Fuel C	-6.0	%	ISO 175
300% Strain，23℃，504 hr，in Reference Fuel C	-18	%	ISO 175
100 ℃, 70 hr, in ASTM # 1 oil	20	%	ISO 175
100% Strain，100℃，70 hr，in ASTM #1 Oil	-5.0	%	ISO 175
300% Strain，100℃，70 hr，in ASTM #1 Oil	10	%	ISO 175
100 ℃, 70 hr, in ASTM # 3 oil	30	%	ISO 175
100% Strain，100℃，70 hr，in ASTM #3 Oil	-8.0	%	ISO 175
300% Strain，100℃，70 hr，in ASTM #3 Oil	12	%	ISO 175
100℃，168 hr，in ASTM #1 Oil	9.0	%	ISO 175
100% Strain，100℃，168 hr，in ASTM #1 Oil	-1.0	%	ISO 175
300% Strain，100℃，168 hr，in ASTM #1 Oil	10	%	ISO 175
100℃，168 hr，in ASTM #3 Oil	30	%	ISO 175
100% Strain，100℃，168 hr，in ASTM #3 Oil	-6.0	%	ISO 175
300% Strain，100℃，168 hr，in ASTM #3 Oil	13	%	ISO 175
100℃，336 hr，in ASTM #1 Oil	7.0	%	ISO 175
100% Strain，100℃，336 hr，in ASTM #1 Oil	-2.0	%	ISO 175
300% Strain，100℃，336 hr，in ASTM #1 Oil	10	%	ISO 175
100℃，336 hr，in ASTM #3 Oil	30	%	ISO 175
100% Strain，100℃，336 hr，in ASTM #3 Oil	-9.0	%	ISO 175
300% Strain，100℃，336 hr，in ASTM #3 Oil	7.0	%	ISO 175
100℃，504 hr，in ASTM #1 Oil	1.0	%	ISO 175
100% Strain，100℃，504 hr，in ASTM #1 Oil	-4.0	%	ISO 175
300% Strain，100℃，504 hr，in ASTM #1 Oil	10	%	ISO 175
100℃，504 hr，in ASTM #3 Oil	7.0	%	ISO 175
100% Strain，100℃，504 hr，in ASTM #3 Oil	-6.0	%	ISO 175
300% Strain，100℃，504 hr，in ASTM #3 Oil	9.0	%	ISO 175
Change rate of ultimate elongation			ASTM D471
23℃，70 hr，in Reference Fuel A（Isooctane）	6.0	%	ASTM D471
23 ℃, 70 hr, methanol	4.0	%	ASTM D471
23℃，168 hr，in Reference Fuel A（Isooctane）	-7.0	%	ASTM D471
23 ℃, 168 hr, methanol	3.0	%	ASTM D471
23℃，336 hr，in Reference Fuel A（Isooctane）	1.0	%	ASTM D471
23℃，336 hr，in Reference Fuel C	4.0	%	ASTM D471
23℃，504 hr，in Reference Fuel A（Isooctane）	1.0	%	ASTM D471
23℃，504 hr，in Reference Fuel C	4.0	%	ASTM D471
100 ℃, 70 hr, in ASTM # 1 oil	18	%	ASTM D471
100 ℃, 70 hr, in ASTM # 3 oil	14	%	ASTM D471
100℃，168 hr，in ASTM #1 Oil	18	%	ASTM D471
100℃，168 hr，in ASTM #3 Oil	15	%	ASTM D471
100℃，336 hr，in ASTM #1 Oil	29	%	ASTM D471
100℃，336 hr，in ASTM #3 Oil	24	%	ASTM D471
100℃，504 hr，in ASTM #1 Oil	29	%	ASTM D471
100℃，504 hr，in ASTM #3 Oil	22	%	ASTM D471
Changes in tensile stress during fracture			ISO 175
23℃，70 hr，in Reference Fuel A（Isooctane）	6.0	%	ISO 175
23 ℃, 70 hr, methanol	4.0	%	ISO 175
23℃，168 hr，in Reference Fuel A（Isooctane）	-7.0	%	ISO 175
23 ℃, 168 hr, methanol	3.0	%	ISO 175
23℃，336 hr，in Reference Fuel A（Isooctane）	1.0	%	ISO 175
23℃，336 hr，in Reference Fuel C	4.0	%	ISO 175
23℃，504 hr，in Reference Fuel A（Isooctane）	1.0	%	ISO 175
23℃，504 hr，in Reference Fuel C	4.0	%	ISO 175
100 ℃, 70 hr, in ASTM # 1 oil	18	%	ISO 175
100 ℃, 70 hr, in ASTM # 3 oil	14	%	ISO 175
100℃，168 hr，in ASTM #1 Oil	18	%	ISO 175
100℃，168 hr，in ASTM #3 Oil	15	%	ISO 175
100℃，336 hr，in ASTM #1 Oil	29	%	ISO 175
100℃，336 hr，in ASTM #3 Oil	24	%	ISO 175
100℃，504 hr，in ASTM #1 Oil	29	%	ISO 175
100℃，504 hr，in ASTM #3 Oil	22	%	ISO 175
The rate of change in Shore hardness			ASTM D471
Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane)	-1.0		ASTM D471
Shore D, 23°C, 70 hr, in Reference Fuel C	-5.0		ASTM D471
Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane)	0.0		ASTM D471
Shore D, 23 ℃, 168 hr, in reference fuel	-6.0		ASTM D471
Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane)	1.0		ASTM D471
Shore D, 23 ℃, 336 hr, in reference fuel C	-5.0		ASTM D471
Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane)	-1.0		ASTM D471
Shore D, 23 ℃, 504 hr, in reference fuel C	-4.0		ASTM D471
Shore D, 100°C, 70 hr, in ASTM #1 Oil	-3.0		ASTM D471
Shore D, 100 ℃, 70 hr, in ASTM # 3 oil	-1.0		ASTM D471
Shore D, 100°C, 168 hr, in ASTM #1 Oil	-3.0		ASTM D471
Shore D, 100 ℃, 168 hr, in ASTM # 3 oil	0.0		ASTM D471
Shore D, 100 ℃, 336 hr, in ASTM # 1 oil	-3.0		ASTM D471
Shore D, 100 ℃, 336 hr, in ASTM # 3 oil	1.0		ASTM D471
Shore D, 100 ℃, 504 hr, in ASTM # 1 oil	-3.0		ASTM D471
Shore D, 100 ℃, 504 hr, in ASTM # 3 oil	-1.0		ASTM D471
The rate of change in Shore hardness			ISO 175
Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane)	-1.0		ISO 175
Shore D, 23°C, 70 hr, in Reference Fuel C	-5.0		ISO 175
Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane)	0.0		ISO 175
Shore D, 23 ℃, 168 hr, in reference fuel	-6.0		ISO 175
Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane)	1.0		ISO 175
Shore D, 23 ℃, 336 hr, in reference fuel C	-5.0		ISO 175
Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane)	-1.0		ISO 175
Shore D, 23 ℃, 504 hr, in reference fuel C	-4.0		ISO 175
Shore D, 100°C, 70 hr, in ASTM #1 Oil	-3.0		ISO 175
Shore D, 100 ℃, 70 hr, in ASTM # 3 oil	-1.0		ISO 175
Shore D, 100°C, 168 hr, in ASTM #1 Oil	-3.0		ISO 175
Shore D, 100 ℃, 168 hr, in ASTM # 3 oil	0.0		ISO 175
Shore D, 100 ℃, 336 hr, in ASTM # 1 oil	-3.0		ISO 175
Shore D, 100 ℃, 336 hr, in ASTM # 3 oil	1.0		ISO 175
Shore D, 100 ℃, 504 hr, in ASTM # 1 oil	-3.0		ISO 175
Shore D, 100 ℃, 504 hr, in ASTM # 3 oil	-1.0		ISO 175
Volume change			ASTM D471
23℃，70 hr，in Reference Fuel A	0.0	%	ASTM D471
23 ℃, 70 hr, methanol	23	%	ASTM D471
23℃，168 hr，in Reference Fuel A	1.0	%	ASTM D471
23 ℃, 168 hr, methanol	24	%	ASTM D471
23℃，336 hr，in Reference Fuel A	1.0	%	ASTM D471
23℃，336 hr，in Reference Fuel C	24	%	ASTM D471
23℃，504 hr，in Reference Fuel A	1.0	%	ASTM D471
23℃，504 hr，in Reference Fuel C	24	%	ASTM D471
100 ℃, 70 hr, in ASTM # 1 oil	-1.0	%	ASTM D471
100 ℃, 70 hr, in ASTM # 3 oil	0.0	%	ASTM D471
100℃，168 hr，in ASTM #1 Oil	-1.0	%	ASTM D471
100℃，168 hr，in ASTM #3 Oil	1.0	%	ASTM D471
100℃，336 hr，in ASTM #1 Oil	-1.0	%	ASTM D471
100℃，336 hr，in ASTM #3 Oil	1.0	%	ASTM D471
100℃，504 hr，in ASTM #1 Oil	-1.0	%	ASTM D471
100℃，504 hr，in ASTM #3 Oil	1.0	%	ASTM D471
Volume change			ISO 175
23℃，70 hr，in Reference Fuel A	0.0	%	ISO 175
23 ℃, 70 hr, methanol	23	%	ISO 175
23℃，168 hr，in Reference Fuel A	1.0	%	ISO 175
23 ℃, 168 hr, methanol	24	%	ISO 175
23℃，336 hr，in Reference Fuel A	1.0	%	ISO 175
23℃，336 hr，in Reference Fuel C	24	%	ISO 175
23℃，504 hr，in Reference Fuel A	1.0	%	ISO 175
23℃，504 hr，in Reference Fuel C	24	%	ISO 175
100 ℃, 70 hr, in ASTM # 1 oil	-1.0	%	ISO 175
100 ℃, 70 hr, in ASTM # 3 oil	0.0	%	ISO 175
100℃，168 hr，in ASTM #1 Oil	-1.0	%	ISO 175
100℃，168 hr，in ASTM #3 Oil	1.0	%	ISO 175
100℃，336 hr，in ASTM #1 Oil	-1.0	%	ISO 175
100℃，336 hr，in ASTM #3 Oil	1.0	%	ISO 175
100℃，504 hr，in ASTM #1 Oil	-1.0	%	ISO 175
100℃，504 hr，in ASTM #3 Oil	1.0	%	ISO 175

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level		UL 94
1.50 mm	HB	UL 94
3.00 mm	V-2	UL 94

Supplementary information	Nominal value	Unit	Test method
Compression load			ASTM D575
10% deflection	2.24	MPa	ASTM D575
15% deflection	3.28	MPa	ASTM D575
2% deflection	0.345	MPa	ASTM D575
20% deflection	4.31	MPa	ASTM D575
25% deflection	5.69	MPa	ASTM D575
5% deflection	1.03	MPa	ASTM D575
50% deflection	15.0	MPa	ASTM D575

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Drying temperature – hot air dryer	100 to 110	°C
Drying time – hot air dryer	2.0	hr
Recommended maximum moisture content	< 0.030	%
Recommended injection volume	40 to 80	%
Proposed maximum recycled material ratio	20	%
Barrel rear temperature	180 to 200	°C
Barrel middle temperature	180 to 205	°C
Barrel front temperature	180 to 210	°C
Nozzle temperature	185 to 210	°C
Processing (melt) temperature	195 to 205	°C
Mold temperature	15 to 40	°C
Injection pressure	41.4 to 103	MPa
Injection speed	Slow-Moderate
Back pressure	1.38	MPa
Screw speed	40 to 80	rpm
Clamping force	4.1 to 6.9	kN/cm²
Cushion	< 3.18	mm
Screw length to diameter ratio	20.0:1.0
Screw compression ratio	2.5:1.0 to 3.0:1.0
Drying temperature	100 to 110	°C
Drying time	2.0	hr
Barrel 1 zone temperature	180 to 200	°C
Barrel 3 zone temperature	180 to 205	°C
Barrel 5 zone temperature	180 to 210	°C
Connector temperature	180 to 210	°C
Melt temperature	190 to 205	°C
Nozzle temperature	185 to 210	°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. Die C
3. Post-cured 16 hr at 230°F
4. Rate A (50°C/h)
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.