| Sparkling clarity and stiffness.&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.30 to 0.60 | % | |
| MD | 0.30 to 0.60 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 2.6 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 20 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 89.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 77.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 103 | ℃ | ISO 306/A50 |
| B50 | 92.0 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | < 100 | mm/min | ISO 3795 |
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 90.0 | % | ISO 13468 |
| Haze | 1.0 | % | ISO 14782 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Dishwasher Test | 300 to 500 | Cycles | USA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 80 | ISO 868 | |
| tensile strength | |||
| fracture | 50.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 6.0 | % | ISO 527-2/5 |
| Bending modulus | 2850 | MPa | ISO 178 |
| bending strength | 97.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 15 to 30 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |