| COLORCOMP* 223RC is an unfilled compound based on Polycarbonate resin. Added features include: Flame Retardant, Mold Release, UV Stabilized. For use in small, intricate parts.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good stripping performance,Flame Characteristics,V-2,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Specific volume | 0.830 | cm³/g | ASTM D792 |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.15 | % | ASTM D570 |
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| Equilibrium, 100 ℃ | 0.58 | % | ASTM D570 |
| Weathering resistance | f1 | UL 746C | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 12 | kJ/m² | ISO 179/1eA |
| 23℃ | 65 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 3200 | J/m | ASTM D4812 |
| 23℃ | 690 | J/m | ASTM D256 |
| -30℃ | 11 | kJ/m² | ISO 180-1A |
| 23℃ | 65 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | No Break | ISO 180/1U | |
| 23℃ | No Break | ISO 180/1U | |
| Drop hammer impact | |||
| 23℃ | 169 | J | ASTM D3029 |
| Tensile impact strength | 546 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 138 | ℃ | ASTM D648 |
| Vicat Softening Temp | 154 | ℃ | ASTM D1525 7 |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 6.8E-5 | 1/℃ | ASTM E831 |
| specific heat | 1260 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | 0.25 | W/m/K | ASTM C177 |
| Relative temperature index | |||
| Electrical performance | 100 | ℃ | UL 746 |
| Strength mechanical performance | 100 | ℃ | UL 746 |
| Impact mechanical performance | 100 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in air | 15 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 3.17 | ASTM D150 | |
| 60 Hz | 3.17 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 1 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 6.00 mm | V-0 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 | |
| Transmittance | |||
| 2540 µm | 88.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 65.5 | MPa | ASTM D638 |
| yield | 62.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 110 | % | ASTM D638 |
| yield | 7.0 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 2340 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 93.1 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 10.0 | mg | ASTM D1044 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 70 | ASTM D785 | |
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 260 to 282 | °C | |
| Barrel middle temperature | 271 to 293 | °C | |
| Barrel front temperature | 282 to 304 | °C | |
| Nozzle temperature | 277 to 299 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.051 in/min |
| 4. 80*10*3 sp=62mm |
| 5. 80*10*3 mm |
| 6. Type S |
| 7. Rate A (50°C/h), Loading 2 (50 N) |
| 8. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |