| About |
|---|
| SABIC® HDPE F01552 is a medium molecular weight High Density Polyethylene specifically designed for blown film extrusion. It has a broad molecular weight with excellent extrudability, high film strength and draw down characteristics. The material contains anti oxidant. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good dissection,Food contact compliance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.15 | g/10min | |
| 190℃，21.6kg | 16 | g/10min | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, MD: 15 µ m, blow molded film | 1400 | MPa | |
| 1% secant, TD: 15 µ m, blow molded film | 1700 | MPa | |
| Tensile strength | |||
| MD: yield, 15 µ m, blow molded film | 31.0 | MPa | |
| TD: yield, 15 µ m, blow molded film | 30.0 | MPa | |
| MD: fracture, 15 µ m, blow molded film | 55.0 | MPa | |
| TD: fracture, 15 µ m, blow molded film | 49.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 15 µ m, blow molded film | 400 | % | |
| TD, fracture, 15 µ m, blow molded film | 610 | % | |
| Drop hammer impact | 180 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD | 4.0 | g | |
| TD | 40 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |