| About |
|---|
| LNP THERMOCOMP UF00ASW is a compound based on Polyphthalamide (PPA) containing glass fiber. Characteristics of this grade of Heat Stabilized and Hot Water Moldable.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.65 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：24 hrs | 0.60 to 0.90 | % | ASTM D955 |
| MD：24 hrs | 0.20 to 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.33 | % | ISO 62 |
| 24hr，50% RH | 0.27 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 19100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 214 | MPa | ISO 527-2/5 |
| yield | 214 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.5 | % | ISO 527-2/5 |
| yield | 1.4 | % | ISO 527-2/5 |
| Bending modulus | 17200 | MPa | ISO 178 |
| 50 mm span | 17500 | MPa | ASTM D790 |
| bending strength | 324 | MPa | ISO 178 |
| Fracture, 50 mm span | 337 | MPa | ASTM D790 |
| Yield, 50 mm span | 335 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 91 | J/m | ASTM D256 |
| 23℃ | 9.4 | kJ/m² | ISO 180-1A |
| 23℃ | 790 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 46 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 6.30 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 3.90 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 281 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 285 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 296 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 297 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 4.3E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 2.4E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 316 to 321 | °C | |
| Barrel front temperature | 327 to 332 | °C | |
| Processing (melt) temperature | 320 to 349 | °C | |
| Mold temperature | 49 to 104 | °C | |
| Back pressure | 0.170 to 0.500 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.051 in/min |
| 3. 0.079 in/min |
| 4. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |