| About |
|---|
| Product Description | |
|---|---|
| Generic | EMA |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| MA content | 14 | wt% | 日本聚乙烯法 |
| Density | 0.935 | g/cm³ | JIS K7112 |
| Melt Flow Rate | 6.0 | g/10min | JIS K6922-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 89 | JIS K7215 | |
| Shaw’s D | 37 | JIS K7215 | |
| Bending modulus | 47 | Mpa | JIS K 6922-2 |
| Tensile modulus | 42 | Mpa | JIS K 6922-2 |
| tensile strength | 9 | Mpa | JIS K6251 |
| yield | 没有屈服点 | Mpa | JIS K 6922-2 |
| fracture | 没有断裂 | Mpa | JIS K 6922-2 |
| Tensile strain | |||
| fracture | >400 | ％ | JIS K6922-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | 190 | kJ/m2 | JIS K 6922-2 |
| Charpy impact strength | 没破坏 | kJ/m2 | JIS K 6922-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | <-70 | ℃ | ISO 974 |
| melting point | |||
| DSC method | 87 | ℃ | JIS K7121 |
| Vicat Softening Temp | 58 | ℃ | JIS K7206 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |