| Material code according to ISO 1043-1: PP Heat stabilized polypropylene reinforced with 50 weight percent long glass fibers. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. (-0403 = heat stabilized, -0453 = low emission) Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Good flexibility,High impact resistance,Chemical coupling,low-temperature impact resistance,Heat Stabilized |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 12000 | MPa | ISO 527-2/1A/1 |
| 80℃ | 8500 | MPa | ISO 527-2/1A |
| tensile strength | |||
| fracture | 145 | MPa | ISO 527-2/1A/5 |
| 80℃ | 90.0 | MPa | ISO 527-2/1A |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2/1A/5 |
| Fracture, 80 ℃ | 2.2 | % | ISO 527-2/1A |
| Bending modulus | ISO 178 | ||
| 23℃ | 12900 | MPa | ISO 178 |
| 80℃ | 9000 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| 23℃ | 235 | MPa | ISO 178 |
| 80℃ | 130 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 38 | kJ/m² | ISO 179/1eA |
| 23℃ | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 75 | kJ/m² | ISO 179/1eU |
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 159 | ℃ | ISO 75-2/A |
| Melting temperature | 165 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 250 to 260 | °C | |
| Barrel middle temperature | 260 to 270 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Nozzle temperature | 280 to 290 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Injection pressure | 60.0 to 120 | MPa | |
| Injection speed | 慢 | ||
| Hold pressure | 40.0 to 80.0 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |