SABIC® HDPE B5260LS

About
SABIC® HDPE B5260LS exhibits good processing properties, typically on high speed extrusion blow moulding machines for UHT milk bottles. Its broad molecular weight distribution offers typically good behaviour during extrusion and blowing, and it is typically used for multi- and mono-layer constructions. Furthermore it has good organoleptic properties, which are required in for example the packaging of dairy products, such as sterilized milk. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE B5260LS exhibits good processing properties, typically on high speed extrusion blow moulding machines for UHT milk bottles. Its broad molecular weight distribution offers typically good behaviour during extrusion and blowing, and it is typically used for multi- and mono-layer constructions. Furthermore it has good organoleptic properties, which are required in for example the packaging of dairy products, such as sterilized milk. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Excellent Processability,Wide molecular weight distribution,Good sensory characteristics.,High density
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.952	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	2.0	g/10min
190℃，21.6kg	60	g/10min
190℃，5.0kg	7.0	g/10min
ESCR(Environmental Stress Cracking Resistance)
10% non-ionic detergent, molded, F50	10.0	hr	ASTM D1693B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, molded	7.0	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	80.0	℃	ISO 75-2/B
Vicat Softening Temp	124	℃	ISO 306/A
Melting temperature
DSC	131	℃	ISO 11357-3
Enthalpy Change	202	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	61		ISO 868
Tensile modulus
2 mm, molded into shape	1100	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	26.0	MPa
Fracture, 2 mm, molded	31.0	MPa
Tensile strain
Fracture, 2 mm, molded	> 200	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1150	MPa	ISO 178
bending strength
2 mm, molded into shape	26.0	MPa	ISO 178

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.