| About |
|---|
| HOPELEN FO-135 is homo polymer resin produced by the polymerization of propylene. This grade is designed to be processed in BOPP film applications. This grade shows good transparence, anti-static and printing properties.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good Printability,Antistatic property,Homopolymer |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 149 | ℃ | ASTM D1525 |
| Melting peak temperature | 160 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 30 µ m, cast thin film | < 0.90 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 99 | ASTM D785 | |
| tensile strength | |||
| yield | 34.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 100 | % | ASTM D638 |
| Bending modulus | 1470 | MPa | ASTM D790 |
| friction coefficient | |||
| Casting thin film | < 1.0 | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |