| Description LUTENE-H BE0400 is an excellent material for blow-molded articles with high density and rigidity. It has good flow characteristics and impact resistance. Applications LUTENE-H BE0400 is used to produce for the following parts. lightweight container from 1 to 10 liters in capacity from 10 to 20 liters in capacity for Jerrican pipes and sheets&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Wide molecular weight distribution,Good liquidity,High density |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.958 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.12 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 25 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | 50.0 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 20℃ | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 130 | ℃ | ASTM D1525 |
| Melting temperature | 134 | ℃ | DSC |
| Hot deformation temperature | 76 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ASTM D2240 | |
| tensile strength | |||
| Yield, 20 ℃ | 30.0 | MPa | ASTM D638 |
| Tensile strain | |||
| 断裂，20℃ | > 500 | % | ASTM D638 |
| Bending modulus | 1100 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 160 to 185 | °C | |
| Barrel 3 zone temperature | 175 to 195 | °C | |
| Barrel 5 zone temperature | 180 to 200 | °C | |
| Connector temperature | 175 to 190 | °C | |
| Melt temperature | 180 to 200 | °C | |
| Nozzle temperature | 160 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |