| PC1800 resin is a medium-high flow (MFR = 18 at 300°C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It is available exclusively at www.sabicpc.com.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Moderate liquidity,Heat Stabilized,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 18 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 17.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 700 | J/m | ASTM D256 |
| 23℃ | No Break | ASTM D4812 | |
| -30℃ | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 70 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | No Break | ISO 180/1U | |
| 23℃ | No Break | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 65.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 124 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 124 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 135 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 135 | ℃ | ASTM D648 |
| Vicat Softening Temp | 141 | ℃ | ASTM D1525 10 |
| B50 | 141 | ℃ | ISO 306 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~95℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM C177 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.6 mm | 27 | kV/mm | IEC 60243-1 |
| 1.6 mm | 27 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Relative permittivity | IEC 60250 | ||
| 60 Hz | 3.00 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| Dissipation factor | IEC 60250 | ||
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 | |
| Refractive index | 1.586 | ISO 489 | |
| Transmittance | |||
| 2540 µm | 88.0 to 90.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | < 0.80 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2350 | MPa | ASTM D638 |
| Tensile modulus | 2350 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 63.0 | MPa | ASTM D638 |
| yield | 63.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | > 70 | % | ASTM D638 |
| fracture | > 70 | % | ISO 527-2/50 |
| yield | 6.0 | % | ISO 527-2/50 |
| yield | 6.0 | % | ASTM D638 |
| Bending modulus | 2300 | MPa | ISO 178 |
| 50 mm span | 2300 | MPa | ASTM D790 |
| bending strength | 90.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 90.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| R-level | 120 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 280 to 300 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 2.0 in/min |
| 4. Type I, 2.0 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. Yield |
| 8. 80*10*3 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |