| EBAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. These resins are less crystalline and softer than polyethylenes. They are non-corrosive at extrusion temperatures and have excellent thermal stability over the full processing temperature range. EBAC+ Specialty Copolymers are produced under patented technology: US Patent 5804675.&& |
| Product Description | |
|---|---|
| Supplier | Westlake Chemical |
| Generic | EBA |
| Material Status | Commercial: Active |
| Features | Good bond,Heat Stabilized |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.45 | g/10min | ASTM D1238 |
| Butyl acrylate composition | 18.0 | wt% | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -73.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 55.0 | ℃ | ASTM D1525 |
| Melting peak temperature | 102 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 40 | ASTM D2240 | |
| tensile strength | |||
| fracture | 14.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 730 | % | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |