| Improved ASA/PC blend for high flow, 1.0mm V0 applications. Improved UV performance aesthetically and physically compared to alternatives.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA+PC |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High liquidity,Halogen free,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2680 | MPa | ASTM D638 |
| Tensile modulus | 2680 | MPa | ISO 527-1-2 |
| tensile strength | ASTM D638 | ||
| yield | 60.0 | MPa | ASTM D638 |
| yield | 65.0 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 61.0 | MPa | ISO 527-2/5 |
| yield | 66.0 | MPa | ISO 527-2/50 |
| fracture | 49.0 | MPa | ASTM D638 |
| fracture | 47.0 | MPa | ASTM D638 |
| fracture | 46.0 | MPa | ISO 527-2/5 |
| fracture | 47.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.0 | % | ASTM D638 |
| Tensile strain | |||
| yield | 4.0 | % | ISO 527-2/5 |
| yield | 4.0 | % | ISO 527-2/50 |
| fracture | 58 | % | ASTM D638 |
| fracture | 31 | % | ASTM D638 |
| fracture | 50 | % | ISO 527-2/5 |
| fracture | 21 | % | ISO 527-2/50 |
| Bending modulus | 2730 | MPa | ISO 178 |
| bending strength | 97.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 90 | J/m | ASTM D256 |
| 23℃ | 330 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| 0℃ | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 13 | kJ/m² | ISO 180-1A |
| Multi axial instrumented impact energy | 85.0 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 81.0 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 64 mm span | 90.0 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| B50 | 96.0 | ℃ | ISO 306 |
| B120 | 98.0 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 6.3E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 6.3E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.00 mm | V-0 | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 30.0 | cm³/10min | ISO 1133 |
| Apparent viscosity of melt | |||
| 260℃，1500 sec^-1 | 105 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 200 to 230 | °C | |
| Barrel middle temperature | 220 to 260 | °C | |
| Barrel front temperature | 230 to 270 | °C | |
| Nozzle temperature | 220 to 260 | °C | |
| Processing (melt) temperature | 230 to 270 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |