| SPESIN® KP212V0是一种聚丁烯对苯二甲酸酯(PBT)产品,。 它可以通过注射成型进行加工,在北美洲、拉丁美洲、欧洲或亚太地区有供货。 特性包括: 阻燃/额定火焰 Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| MD | 1.8 to 2.6 | % | ASTM D955 |
| TD | 1.9 | % | ISO 294-4 |
| MD | 1.9 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 60% RH | 0.060 | % | ASTM D570 |
| 23℃，24hr | 0.13 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.2 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 35 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ASTM D648-A |
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 165 | ℃ | ASTM D648-A |
| Melting peak temperature | 224 | ℃ | ASTM D3418 |
| Melting temperature | 223 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 25 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 3.20 | ASTM D150 | |
| Arc resistance | 85.0 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 55.0 | MPa | ISO 527-2 |
| 23℃ | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 11 | % | ASTM D638 |
| Fracture, 23 ℃ | 4.3 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2410 | MPa | ISO 178 |
| 23℃ | 2630 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 85.0 | MPa | ISO 178 |
| 23℃ | 98.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 118 | ISO 2039-2 | |
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 100 to 120 | °C | |
| Drying time – hot air dryer | 3.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel rear temperature | 240 | °C | |
| Barrel middle temperature | 245 | °C | |
| Barrel front temperature | 250 | °C | |
| Nozzle temperature | 250 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |