TAFMER™ XM-7080

About
TAFMER™ XM-7080 TAFMER™ XM is a superior, low crystalline copolymer of propylene and alpha-olefin which is perfect for biaxially oriented polypropylene (PP) and cast film sealant as well as a resin modifier for polyolefins. TAFMER XM is developed with Metallocene catalyst. The material has excellent low temperature sealability, good sealing performance in a wide temperature range and good anti-blocking properties. As a heat seal layer for OPP film, TAFMER XM is an excellent package sealer for chocolates, cookies and crackers among other items. In addition, the low temperature shrink characteristics of PP can be improved with TAFMER XM.&&TAFMER™ XM-7080 TAFMER™ XM-7080, propylene based polymer, is a specialty olefinic resin designed to improve heat sealing behavior of Polypropylene (PP) based film.&&

About

TAFMER™ XM-7080 TAFMER™ XM is a superior, low crystalline copolymer of propylene and alpha-olefin which is perfect for biaxially oriented polypropylene (PP) and cast film sealant as well as a resin modifier for polyolefins. TAFMER XM is developed with Metallocene catalyst. The material has excellent low temperature sealability, good sealing performance in a wide temperature range and good anti-blocking properties. As a heat seal layer for OPP film, TAFMER XM is an excellent package sealer for chocolates, cookies and crackers among other items. In addition, the low temperature shrink characteristics of PP can be improved with TAFMER XM.&&TAFMER™ XM-7080 TAFMER™ XM-7080, propylene based polymer, is a specialty olefinic resin designed to improve heat sealing behavior of Polypropylene (PP) based film.&&

Product Description
Supplier	Mitsui
Generic	PAO
Material Status	Commercial: Active
Features	Good Clarity,Good surface appearance,Good Hardness,Thermal viscous strength,High Heat Resistance,Low odor,High scratch resistance,Low temperature heat sealing
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate
230℃，2.16kg	7.0	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	55		ASTM D2240
Tensile modulus	390	MPa	ASTM D638
tensile strength
fracture	36.0	MPa	ASTM D638
yield	13.0	MPa	ASTM D638
Tensile strain
fracture	> 600	%	ASTM D638

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	74.0	℃	ASTM D1525
Melting temperature	83.0	℃	ASTM D2117

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.