| About |
|---|
| NYLOY® PG-2040N is a Polypropylene material filled with 40% glass fiber. It is available in Asia Pacific or North America for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Nytex |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.10 | g/cm³ | ASTM D792 |
| — | 1.27 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.48 | % | ASTM D955 |
| TD | 1.0 | % | ASTM D955 |
| TD | 1.0 | % | ISO 294-4 |
| MD | 0.48 | % | ISO 294-4 |
| Ash Content | 45 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 83 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 154 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 140 | ℃ | ISO 75-2/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 106 | ASTM D785 | |
| R-level | 98 | ISO 2039-2 | |
| tensile strength | |||
| — | 80.4 | MPa | ASTM D638 |
| — | 81.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| — | 7360 | MPa | ASTM D790 |
| — | 6500 | MPa | ISO 178 |
| bending strength | |||
| — | 123 | MPa | ASTM D790 |
| — | 130 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Processing (melt) temperature | 180 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |