| High performance blown film resin for flexible packaging Excellent abuse resistance Low temperature seal initiation Excellent optics Outstanding high oxygen transmission rates Complies with: U.S. FDA FCN 424 Canadian HPFP No Objections EU, No 10/2011 U.S. FDA-DMF Consult the regulations for complete details. AFFINITY* PF 1140G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed to be used in a variety of demanding applications including form-fill-seal packaging and fresh produce bags. This resin has excellent compatibility with other polyolefins, allowing efficient blending and coextrusion.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | POP |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.897 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.6 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 51 | µm | |
| Membrane puncture strength | |||
| 51 µm | 8.18 | J | Internal Method |
| Membrane puncture force | |||
| 51 µm | 83.6 | N | Internal Method |
| Membrane puncture resistance | |||
| 51 µm | 20.3 | J/cm³ | Internal Method |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 51 µ m | 72.8 | MPa | |
| 2% secant, TD: 51 µ m | 73.2 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, yield, 51 µ m | 5.79 | MPa | |
| TD, yield, 51 µ m | 6.34 | MPa | |
| MD, fracture, 51 µ m | 50.3 | MPa | |
| TD, fracture, 51 µ m | 39.5 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 51 µ m | 690 | % | |
| TD, fracture, 51 µ m | 700 | % | |
| Drop hammer impact | |||
| 51 µm | > 850 | g | ASTM D1709-B |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：51 µm | 470 | g | |
| TD：51 µm | 620 | g | |
| Initial sealing temperature | |||
| 51 µm | 81.1 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 76.7 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 96.1 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，50.8 µm | 134 | ASTM D2457 | |
| transparency | |||
| 50.8 µm | 70.0 | ASTM D1746 | |
| Haze | |||
| 50.8 µm | 1.3 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 209 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Modified rectangular test specimen. |
| 3. Temperature at which 2 lb/in. (8.8 N/25.4 mm) heat seal strength is achieved. Heat Seal Strengths, Topwave HT Tester 0.5 S dwell, 40 psi bar pressure, pull speed 10 in./min (250 mm/sec). |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |