| Description High Transparency, Heat Resistance, Chemical Resistance Application Refrigerator Sleeves, Miscellaneous&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | Good Clarity,Heat Resistance, Good,Solvent resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 200℃，10.0kg | 29 | g/10min | ASTM D1238 |
| 200℃，3.80kg | 10 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 3.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD: 3.2 mm, injection molded | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30 ℃, 6.4mm, injection molding | 9.8 | J/m | ASTM D256 |
| 23 ℃, 6.4mm, injection molding | 9.8 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm span | 90.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 5 |
| Relative temperature index | |||
| Electrical performance | 50.0 | ℃ | UL 746 |
| Strength mechanical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23 ℃, 3.20 mm, injection molding | 3110 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃, 3.20 mm, injection molding | 73.5 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.20 mm, injection molding | 6.0 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, 3.20 mm, injection molding | 3680 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 23 ℃, 3.20 mm, injection molding | 118 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-grade, 23 ℃, injection molding | 123 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel rear temperature | 170 to 190 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Nozzle temperature | 190 to 220 | °C | |
| Processing (melt) temperature | 190 to 220 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |