| About |
|---|
| Adflex KS 021 P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. It is suitable for the extrusion and calendering of soft film and sheet, for the impact modification of polypropylene, as well as monolayer and multilayer air quenched blown films. It is also used by our customers as high cold impact resistance material for automotive color-matched interior trim applications. Key characteristics are flexibility and low temperature impact resistance. The grade is available in natural pellet form.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Good flexibility,Solvent resistance,low-temperature impact resistance,High ESCR |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.880 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.90 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 38 | ISO 868 | |
| tensile strength | |||
| Fracture, 23 ℃ | 13.0 | MPa | ISO 527-2/50 |
| Yield, 23 ℃ | 8.00 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 800 | % | ISO 527-2/50 |
| Yield, 23 ℃ | 38 | % | ISO 527-2/50 |
| Bending modulus | |||
| String, 23 ℃ | 300 | MPa | ISO 178 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 85.0 | kN/m | ASTM D624 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40 ℃, localized fracture | 86 | kJ/m² | ISO 180-1A |
| 23 ℃, localized fracture | 52 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -40℃，3.20 mm，Energy at Peak Load，Brittle Failure | 23.0 | J | ASTM D3763 |
| 23℃，3.20 mm，Energy at Peak Load，Ductile Failure | 17.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 38.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 48.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 67.0 | ℃ | ISO 306/A50 |
| Melting temperature | 161 | ℃ | ISO 11357-3 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 21.7 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |